The Eusebius-copying and more

Noah's ark: new in Muschelkalk limestone, old in Ettringer tuff stone. Tower of St. Eusebius' Church

Noah's ark: new in Muschelkalk limestone, old in Ettringer tuff stone

← to the first post on this restoration project

As I already explained in reported yesterday I am currently carving corbels for the tower of the St. Eusebius's Church in Arnhem (the Netherlands). The small reliefs that I am carving now generally don't have too many details. To a large extent this is because the Ettringer tuff stone in which it was originally carved, isn't very suited for detailed carving: it contains fairly large, sandy bimsspots, that later often wash out, leaving large holes in the stone surface. You might try to carve something in that spot, but your chisel will sink in, unless you have a very wide chisel. You can see those yellow soft spots very well in the picture above.

The replacement stone is Muschelkalk limestone, a fairly coarse limestone from Germany that matches the character of the tufa around it very well, but is a lot easier to carve and detail in, and apparently is more weather-resistant as well. Because the grain of the Muschelkalk is finer, I also got the opportunity to add a little more detail, but without departing too much from the original . The idea is that the sculptors would have added more detail if the tuff had allowed it.

This ark was really something to enhance a bit. With a few windows and the planks of the ship's hull (the waves were already there, but they were very weathered) it's immediately a lot more attractive.

a corbel with anchor, tower of  St. Eusebius's Church (Arnhem)

Anchor, new and old

And then you'll be right on the old debate: what is restoration? Are you going to copy exactly what was there, without adding anything, or is there some room for that little bit extra? These are things I don't think up all on my own. But I am happy with the outcome, it's quite a bit more interesting for me this way, because I don't have to just slavishly copy what was already there, but can put something of myself in it.

The old work has something very playful, what must be a result of carving in the direct carving method, and only after a round on the scaffolding around the tower, I began to see it. That's why the new work should preferably also have that directness, with traces of the chiseling still visible, and carved not quite super crisp and clean. spikes new and oldAnd therefore the Muschelkalk is such a good choice: that coarseness of the tuff partly returns in the new stone, but something more can be made of it.

But there are also little reliefs that are absolutley unclear as to what they portray. On the left a picture: it is a couple of spiky protrusions, perhaps with a band surrounding it. If you know what it is you tell me. After a brief discussion it was decided to let the mystery be, and I copied it without much changes.

→ Read more… is the blog of Koen van Velzen, sculptor in stone and bronze. Look up my website as well: